| Conductor |
| Material |
CCA (Copper content: 22%–31%) |
| Diameter |
0.5 mm ± 0.01 mm |
| Wire Gauge |
24 AWG |
| Insulation |
| Material |
HDPE |
| Thickness |
0.18 mm |
| Diameter |
0.90 mm ± 0.06 mm |
| Color |
Blue, white/blue; orange, white/orange; green, white/green; brown, white/brown |
| Rip Cord |
| Material |
Polyester fiber |
| Specification |
500D |
| Sheath |
| Material |
FR-PVC (ROHS compliant) |
| Min. Average Thickness |
0.5 mm |
| Diameter |
5.1 mm ± 0.3 mm |
| Color |
Orange |
| Electrical |
| Max. DC Resistance of a Single Conductor |
14.5 Ω/100 m (14.5 Ω/328.08 ft) |
| Min. Insulation Resistance |
5000 MΩ/km |
| Max. DC Resistance Unbalance |
2% (pair intra), 4% (pairs inter) |
| Max. Mutual Capacitance |
5.6 nF/100 m (5.6 nF/328.08 ft) |
| Dielectric Strength |
No breakdown with 1kV DC for 1 min |
| Mechanical |
| Tensile Strength |
Sheath ≥13.5 MPa, insulation ≥16 MPa |
| Elongation at Break |
Sheath ≥150%, insulation ≥300% |
| Installation Bending Radius |
>8 times of the outer cable diameter |
| Conductor Elongation at Break |
≥8% |
| Environmental |
| Shrinkage of Insulation |
≤5% |
| Color Migration Resistance of Insulation |
No migration |
| Sheath Tensile Strength and Elongation at Break after Aging |
≥12.5 MPa, ≥100% |
| Low Temperature Bending Test |
No cracking after the test |
| Heat Shock Test |
No cracking after the test |
| Operation Temperature |
–20 °C to +60 °C (–4 °F to +140 °F) |
| Installation Temperature |
0 °C to +50 °C (32 °F to 122 °F) |
| Storage Temperature and Humidity |
–10 °C to +40 °C (14 °F to 104 °F), <60% (RH) |
| Security |
| Vertical Fire Propagation Test |
Comply with IEC 60332-2-2 |
| Packaging |
| Cable Length |
100 m ± 1 m (328.08 ft ± 3.28 ft) |
| Net Weight |
2 kg ± 0.4 kg (4.41 lb ± 0.88 lb) |
| Gross Weight |
10.8 kg ± 0.8 kg (23.81 lb ± 1.76 lb) |
| Inner Carton Dimensions |
220 mm × 220 mm × 105 mm (L × W × H) |
| Packaging Dimensions |
537 mm × 242 mm × 253 mm (L × W × H) |